Title: | Korozyon Önleyici Uygulamalar için Grafen Oksit - Epoksi Baz Astar Nanokompozit Kaplama Geliştirme | Other Titles: | Development of Graphene Oxide - Epoxy Base Primer Nanocomposite Coatings for Anti-Corrosion Application | Authors: | Bilgin, Taha | Advisors: | Tutumlu, Zeynep Büke, Zarife Göknur |
Keywords: | Mühendislik Bilimleri Engineering Sciences Atmosferik korozyon Atmospheric corrosion ; Yüzey kaplama malzemeleri Surface coating materials |
Publisher: | TOBB Ekonomi ve Teknoloji Üniversitesi | Source: | Bilgin, Taha. (2021). Korozyon önleyici uygulamalar için grafen oksit - epoksi baz astar nanokompozit kaplama geliştirme. (Yayınlanmamış Yüksek Lisans Tezi). TOBB Ekonomi ve Teknoloji Üniversitesi, Fen Bilimleri Enstitüsü, Mikro ve Nanoteknoloji Ana Bilim Dalı | Abstract: | Grafen oksitin (GO) kromat içermeyen epoksi baz astarın (EBP) korozyon önleme direncine olan etkisi araştırılmıştır. Nanokompozit kapmalar, ağırlıkça %0,25, %0,5, %0,75 ve %1 GO içerecek şekilde hazırlanmış ve kaplama kalınlığı 50 µm'yi geçmeyecek şekilde uygulanmıştır. GO kullanılmadan önce Taramalı Elektron Miktoskobu (SEM), Raman Spektroskobisi ve Fourier Dönüşümlü Kızılötesi Spektroskopisi (FTIR) kullanılarak karakterize edilmiştir. Optik tensiyometre ile ölçülen yüzey gerilim açıları, GO – EBP nanokompozitlerin, yalın EBP kaplamaya göre daha hidrofobik olduğunu göstermiştir. En yüksek yüzey gerilim açısı ağırlıkça %0,75 GO içeren nanokompozit kaplamada elde edilmiştir. Kaplamanın korozyon direncinin analiz edilebilmesi için Tuz Sisi Püskürtme testi gerçekleştirilmiştir. Kaplamanın termal davranışı Diferansiyel Taramalı Kalorimetre (DSC) ve Termogravimetrik Analiz (TGA) ile incelenmiştir. The effect of graphene oxide (GO) on the corrosion protection of non-chromate epoxy base primer (EBP) was investigated. Nanocomposite coatings, less than 50 µm thickness, were prepared adding various amount of (0.25, 0.5, 0.75, 1 wt%) GO and characterized using Scannig Electron Microscopy (SEM), Fourier Transform Infrared Spectroscopy (FTIR) and Raman Spectroscopy. Contact angle measurement results revealed that GO – EBP nanocomposites are more hydrophobic than neat EBP. The higher contact angle result was obtained for EBP containing 0.75 wt% of GO. Optical tensiometer and salt spray fog testing were used to charactarize the protection performance of coatings. The thermal behaviour of the coating had been investigated by using Differential Scanning Calorimetry (DSC) and Thermogravimetric Analysis (TGA). |
Description: | YÖK Tez No: 686894 | URI: | https://tez.yok.gov.tr/UlusalTezMerkezi/TezGoster?key=v7BkNnnepTnbhn8rNR77Ld6bS2qDYSNS-vLAotb9GUxu_KR_Sj87KTv_51PdZw4V https://hdl.handle.net/20.500.11851/7965 |
Appears in Collections: | Mikro ve Nanoteknoloji Yüksek Lisans Tezleri / Micro- and Nano-Technology Master Theses |
Files in This Item:
File | Size | Format | |
---|---|---|---|
686894.pdf | 2.15 MB | Adobe PDF | View/Open |
CORE Recommender
Page view(s)
630
checked on Dec 23, 2024
Download(s)
186
checked on Dec 23, 2024
Google ScholarTM
Check
Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.